期刊
CERAMICS INTERNATIONAL
卷 44, 期 15, 页码 18528-18534出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2018.07.074
关键词
Cultural heritage material; Changsha kiln; Epsilon-Fe2O3; Brown glaze; Green glaze; Changsha porcelain
资金
- National Natural Science Foundation of China [41103013]
- Science and Technology Commission of Guangdong Province Project [20158030803055]
- Focused Research and Development of Hunan Province Project [2016SK2017]
- CAI YUANPEI 2016-18 program [36708RD]
Changsha kiln was an ancient factory from the Tang Dynasty (618-907 CE) to the Five Dynasties (907-960 CE), famous for its colored porcelain production. It was one of the pioneer sites to master the poly-color technique at high temperature. In this work, by using Energy Dispersive X-Ray Fluorescence (EDXRF), Raman spectroscopy and Scanning Electron Microscopy Energy Dispersive X-ray Spectrometer (SEM-EDS), the composition and structure of two of its emblematic colored glazes were studied. The results confirmed that the chromogenic elements of brown and green colored glazes are well iron and copper respectively. They also revealed a significant presence of hematite (alpha-Fe2O3) phase with dendritic shape close to the glaze surface and oddly a substantial amount of epsilon-Fe2O3 phase at the body/glaze interface. It is the second type of ancient Chinese glaze in which the very rare and metastable iron(III) oxide polymorph was found. No Cu-based particle was identified in green glaze. The green color is certainly due to Cu2+ dispersed in the glassy matrix. Our study confirmed that Cassiterite (SnO2) was used as opacifier compound to obtain opaque green color.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据