Preparation of in situ grown silicon carbide whiskers onto graphite for application in Al2O3-C refractories

C-SiC composite powders were prepared by salt-assisted synthesis from Si powders, graphite, and a molten salt medium (NaCl and NaF) with the molar ratio of Si/C = 1/2 at 1300 degrees C for 3 h. After the C-SiC composite powders part and complete replacement of the graphite, the mechanical properties, oxidation resistance and slag-corrosion resistance of the Al2O3-C materials were studied by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS), as well as with dedicated equipment. The results indicated that SiC whiskers, with lengths of 10-50 nm, formed on the surface of the flake graphite, and the activation energy of oxidation of the C-SiC composite powder increased by 45.72 kJ mot(-1) as compared to that of flake graphite. Furthermore, the decarburization area and slag erosion area of the Al2O3-C material decreased after 3 wt% of C-SiC composite powder was substituted for the flake graphite. Meanwhile, the cold modulus of rupture was maintained when 3 wt% of C-SiC composite powder was added. This improved both the oxidation and slag resistance of the Al2O3-C materials.