Flexural strength evaluations and fractography analyses of slip cast mesoporous submicron alumina

期刊

CERAMICS INTERNATIONAL
卷 44, 期 5, 页码 5193-5201

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2017.12.125

关键词

Flexural strength; Mesoporous alumina; Submicron; Transgranular fracture; Intergranular fracture; Slip casting

资金

  1. CCMX, Switzerland
  2. Bobst Mex SA [5211.00093.100.01]

向作者/读者索取更多资源

Mesoporous submicron alpha-Al2O3 green compacts were fabricated using slip casting of ultrafine alumina powders. The pre-sintered samples were sintered in air atmosphere at 1300 degrees C, 1350 degrees C, 1400 degrees C, and 1500 degrees C to obtain a variety of grain morphologies namely submicron equiaxed and micro rod structures. The resulting grain diameters lie between similar to 270 nm and similar to 1590 nm and total porosity fraction between 0.05% and 13%. The room temperature flexural strength (sigma) evaluations and fractography analyses of sintered alumina samples were performed. It was observed that the total porosity fraction dictates the flexural strength as compared to grain diameter. Further, it was found that the flexural strength exhibited a decreasing trend for an increase in the total porosity fraction, and proved to be a better effective parameter than open porosity fraction. The fractography analyses suggest that samples sintered at 1300 degrees C and 1350 degrees C predominantly underwent intergranular fracture, while those sintered at 1400 degrees C and 1500 degrees C underwent a mixture of intergranular and transgranular fracture.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据