This paper reports results of strength and reaction products of blast-furnace slag cements activated using a mixture of MgO-NaOH with a ratio 50/50 incorporated at 4, 6 and 8% relative to the slag mass. Pastes and mortars were prepared and cured at 20 degrees C and 60 degrees C-24 h-20 degrees C up to 90 days. The results indicated that the combination of MgO-NaOH acts as an effective alkaline activator of the slag, as samples cured at 20 degrees C developed 54 MPa at 90 days, while those at 60 degrees C-24 h-20 degrees C had a rapid strength gain at early ages but in the long run strengths of similar to 42 MPa at 90 days were observed. The microstructures consisted of (C-(A)-S-H), third aluminate hydrates and hydrotalcite. The formation of the latter increased at higher MgO:NaOH concentration lowering the Al uptake by C-S-H. MgO and Mg(OH)(2) were not detected, indicating an effective incorporation of Mg2+ ions into the atomic structure of the reaction products.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据