Palladium coatings; CVD process; Degradation; Oxidation
资金
- National Science Centre, Poland (NCN) [2015/19/B/ST8/01645]
Palladium layer (7 mu m thick) was deposited on the surface of the Inconel 713 LC, Inconel 625 and CMSX 4 Ni-base superalloys by the electroplating method. Electroplated samples were annealed at 1050 degrees C for 2 h in the argon atmosphere. The aluminide coatings were deposited by the CVD method. The nonmodified aluminide coating consists of the NiAl phase. Palladium modification let to formation of the (Ni, Pd) Al phase in coatings. The palladium modified as well as nonmodified coatings were oxidized at 1100 degrees C in the air atmosphere. For both Inconel 713 LC and CMSX 4 superalloys palladium modified coatings show better oxidation resistance than nonmodified ones. Palladium inhibits the outward diffusion of substrate elements (cobalt and chromium) during oxidation of the aluminide coating. Moreover, it stabilizes the beta-NiAl phase, keeps the higher content of aluminum in the beta-NiAl phase for a long time and thus increases the lifetime of the coated substrate. (C) 2017 Politechnika Wroclawska. Published by Elsevier Sp. z o.o. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据