期刊
APPLIED SURFACE SCIENCE
卷 440, 期 -, 页码 790-803出版社
ELSEVIER
DOI: 10.1016/j.apsusc.2018.01.226
关键词
Ni-based single crystal superalloy; Oxidation mechanism; Surface roughness; External diffusion flux of Al; Protective alpha-Al2O3 film
类别
资金
- National Natural Science Foundation of China [51375388]
- Fundamental Research Funds for the Central Universities [3102017gx06002]
The high-temperature oxidation dynamics and mechanisms of a Ni-based single crystal superalloy with four kinds of surface roughnesses were investigated by virtue of XRD, OM, SEM and EDS at 1000 degrees C. In the initial oxidation stage, outer (Ni, Co)O was mainly produced on the surfaces of the samples with Ra = 90 nm and 19 nm. Correspondingly, outer Cr2O3 and transient theta-Al2O3 were mainly formed on the surfaces with Ra = 509 nm and 182 nm. After 180 min oxidation, the values of instantaneous parabolic mass gain coefficients (k(p)) of the samples with all surface roughnesses were gradually consistent with the data of the growth parabolic coefficient of alpha-Al2O3. The oxidation mechanisms of Ni-based superalloy with different surface roughnesses were discussed by a model. The external diffusion flux of Al (D-Al) increases with the increases of surface roughness. Thus, the required Al concentration decreases with the increases of surface roughness when the selective oxidation of Al occurrs to form a protective single alpha-Al2O3 film. (C) 2018 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据