APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING
卷 124, 期 6, 页码 -出版社
SPRINGER
DOI: 10.1007/s00339-018-1835-7
关键词
-
In this work, colloidal spherical nanoparticles NPs of silicon carbide SiC have been synthesized using second harmonic generation 532 nm Nd:YAG laser ablation of silicon target dipped in ethanol solution at various laser fluences (1.5-5) J/cm(2). X-Ray diffraction XRD, scanning electron microscopy SEM, transmission electron microscope TEM, Fourier transformed infrared spectroscopy FT-IR, Raman spectroscopy, photoluminescence PL spectroscopy, and UV-Vis absorption were employed to examine the structural, chemical and optical properties of SiC NPs. XRD results showed that all synthesised SiC nanoparticles are crystalline in nature and have hexagonal structure with preferred orientation along (103) plane. Raman investigation showed three characteristic peaks 764,786 and 954 cm(-1), which are indexing to transverse optic TO phonon mode and longitudinal optic LO phonon mode of 4H-SiC structure. The optical absorption data showed that the values of optical energy gap of SiC nanoparticles prepared at 1.5 J/cm(2) was 3.6 eV and was 3.85 eV for SiC synthesised at 5 J/cm(2). SEM investigations confirmed that the nanoparticles synthesised at 5 J/cm(2) are agglomerated to form larger particles. TEM measurements showed that SiC particles prepared at 1.5 J/cm(2) have spherical shape with average size of 25 nm, while the particles prepared at 5 J/cm(2) have an average size of 55 nm.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据