RARE METAL MATERIALS AND ENGINEERING
卷 45, 期 7, 页码 1709-1713出版社
NORTHWEST INST NONFERROUS METAL RESEARCH
DOI: 10.1016/S1875-5372(16)30145-X
关键词
electroless plating; reducing agent; ABS resin material; adhesion strength
资金
- Provincial Natural Science Foundation of Zhejiang [Y14E010005]
An environment-friendly surface etching and activation technique for ABS surface metallization were investigated as a replacement for conventional chromic acid etching bath and palladium catalyst. After etching by H2SO4-MnO2 colloid, the ABS surfaces became rough; meanwhile the carboxyl and hydroxyl groups were formed on the surface. With absorption and reduction by a sodium borohydride solution, copper particles were deposited on the ABS surface, which serve as a catalyst replacement for SnCl2/PdCl2 colloid. The effects of CuSO4 concentration, NaBH4 concentration, reduction temperature and reduction time on the adhesion strength between the ABS surface and the electroless copper film were investigated. The average adhesion strengths reaches 0.87 kN.m(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据