期刊
ACTA MATERIALIA
卷 145, 期 -, 页码 196-209出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2017.11.057
关键词
Interface plane distribution; Habit plane; Phase transformation path; Crystallography; Orientation relationship; Duplex stainless steel
资金
- Deakin Advanced Characterisation Facility
- Australian Research Council
The effect of the ferrite to austenite phase transformation route on the microstructure and interface plane character distributions was studied in a duplex stainless steel. Two markedly different austenite morphologies (i.e., equiaxed and Widmanstatten) were produced through diffusional (slow cooling) and semi-shear (air-cooling) transformations, respectively. Both austenite morphologies had textures similar to the as-received condition, which was attributed to a texture memory effect. The air-cooled microstructure displayed a significantly higher content of Kurdjumov-Sachs (K-S) and Nishiyama-Wassermann (N-W) interfaces (39%) compared with the slow-cooled one (16%), due to the change in the austenite nucleation and growth mechanism during the phase transformation. A five-parameter analysis of different interfaces revealed that for K-S/N-W orientation relationships, ferrite and austenite terminated on (110) and (111) planes, respectively, regardless of the transformation route. The population of these planes, however, increased as the transformation rate increased. A higher fraction of Sigma 3 boundaries was observed in the equiaxed austenite morphology compared with its Widmanstatten counterpart, which was mainly attributed to the different kinetics and the growth mode of austenite plates during the phase transformation. Sigma 9 boundaries were mostly formed where two Sigma 3 boundaries met and were largely of tilt character because of geometric constraints. The intervariant boundary plane distributions of both austenite microstructures displayed more frequent OM orientations than other planes for a majority of the boundaries. This trend was markedly stronger for Widmanstatten austenite. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据