Autonomously self-healing hydrogels have received considerable attentions due to their capacity for repairing themselves spontaneously after suffering damage, which can provide a better stability and a longer life span. In this work, a robust and mechanically and electrically self-healing hydrogel with an efficient electromagnetic interference (EMI) shielding performance was successfully fabricated via the incorporation of multiwalled carbon nanotubes (MWCNTs) into the hydrophobically associated polyacrylamide (PAM) hydrogels by using cellulose nanofiber (CNF) as the dispersant. It was been found that CNF could not only assist the homogeneous dispersion of MWCNTs but also effectively enhance the mechanical property of the resultant hydrogels. As a result, the optimal tensile strength (approximate to 0.24 MPa), electrical conductivity (approximate to 00.85 S m(-1)), and EMI shielding effectiveness (approximate to 28.5 dB) were achieved for the PAM/CNF/MWCNT composite hydrogels with 1 wt % MWCNTs and 0.3 wt % CNF, which showed 458, 844, and 90% increase over (approximate to 0.043 MPa, approximate to 0.09 S m(-1), and, approximate to 15 dB, respectively) the PAM hydrogel. More encouragingly, these composite hydrogels could rapidly restore their electrical conductivity and EMI shielding effectiveness after mechanical damage at room temperature without any external stimulus. With outstanding mechanical and self healing properties, the prepared composite hydrogels were similar to human skin, but beyond human skin owing to their additional satisfactory electrical and EMI shielding performances. They may offer promising and broad prospects in the field of simulate skin and protection of precision electronics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据