4.8 Article

Oligosilylarylnitrile: The Thermoresistant Thermosetting Resin with High Comprehensive Properties

期刊

ACS APPLIED MATERIALS & INTERFACES
卷 10, 期 14, 页码 11933-11940

出版社

AMER CHEMICAL SOC
DOI: 10.1021/acsami.8b00238

关键词

oligosilylnitrile; polysilazane; thermal cure; thermoresistant; mechanical property

资金

  1. Research Institute for Special Structures of Aeronautical Composite, Aviation Industry Corporation of China [527859-01]

向作者/读者索取更多资源

One of the highest thermoresistant thermosetting resins ever studied so far, oligosilylarylnitrile resin, was investigated first in this study. Oligosilylarylnitrile was synthesized by lithium-reduced Wurtz-Fittig condensation reaction, and the prepared viscous resin exhibited moderate rheological behaviors while heated purely or together with 20% polysilazane as a cross-linking agent. The thermal curing temperature's were found by differential scanning calorimetry at 268 degrees C (pure) and 158 degrees C (with the polysilazane cross-linking agent), which is comparably close to that of polysilylarylacetylene resin (normally at 220-250 degrees C) but much lower than those of polyimide and phthalonitrile resins (normally >300 degrees C), indicating the admirable material processability of oligosilylnitrile. The cured oligosilylarylnitrile resins have extremely high thermal resistance, indicated by the results of thermogravimetric analysis (the mass residue at 800 degrees C is >90% under N-2) and dynamic mechanical analysis (the glass transition temperature is >420 degrees C): The mechanical property of the oligosilylarylnitrile-matrixed silica-cloth reinforced laminate is comparably close to those of polyimide and phthalonitrile but much higher than that of polysilylarylactylene, indicating the enviable thermal and mechanical properties of oligosilylnitrile. Thus, among the high-temperature resins ever studied so far, the oligosilylarylnitrile resin was found to have the almost best comprehensive characteristics of processability and properties.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据