ACS APPLIED MATERIALS & INTERFACES
卷 10, 期 21, 页码 18327-18337出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.8b03757
关键词
anion exchange membranes; fuel cells; flexible multication side chain; triblock copolymers; ion conduction
资金
- National Nature Science Foundation of China [21576226, 21376194, 21736009]
To achieve highly conductive and stable anion exchange membranes (AEMs) for fuel cells, novel triblock copolymer AEMs bearing flexible side chain were synthesized. The triblock structure and flexible side chain are responsible for the developed hydrophilic/hydrophobic phase separated morphology and well-connected ion conducting channels, as confirmed by transmission electron microscopy. As a result, the triblock copolymer AEMs with flexible side chain (ABA-TQA-x) demonstrated considerably higher conductivities, up to 130.5 mS cm(-1) at 80 degrees C, than the AEMs with monocation side chain (ABA-MQA). Furthermore, the long alkyl spacer between the backbone and quaternary ammonium groups, as well as long intercation spacer limits the water swelling of the membranes to some degree, resulting in good alkaline stability. The ABA-TQA-44 membrane retained 84.7% and 83.1% of its original conductivity and ionic exchange capacity, respectively, after immersed in a 1 M aqueous KOH solution at 80 degrees C for 480 h. Furthermore, the peak power density of a H-2/O-2 single cell using ABA-TQA-44 is 204.6 mW cm(-2) at a current density of 500 mA cm(-2) at 80 degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据