期刊
ACS ENERGY LETTERS
卷 2, 期 3, 页码 544-548出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsenergylett.7b00007
关键词
-
类别
资金
- Israel Science Foundation (ISF)
- INREP projec
- Israel Ministry of Science and Technology
- Israel India binational collaboration program
Li- and Mn-rich layered oxide cathodes are known to suffer from capacity fading and average discharge voltage decay upon cycling. In the present study, the improved cycling stability of a Li and Mn-rich cathode Li1.2Ni0.27Mn0.40Co0.13O2 in full cells is reported. The electrochemical performance of the Li- and Mn-rich cathodes comprising Li1.2Ni0.13Mn0.54Co0.13O2 and Li1.2Ni0.27Mn0.40Co0.13O2 was tested in Li-ion full cells with graphite as anode material at 30 C-circle. The full cells with Li1.2Ni0.13Mn0.54Co0.13O2 cathodes exhibited initially high capacities of about 250 mAh g(1), which fades rapidly to 130 mAh g(-1) after 120 cycles at C/5 rate. However, full cells comprising Li1.2Ni0.27Mn0.40Co0.13O2 cathodes exhibited an initial capacity of about 190 mAh g(-1) with very stable cycle-life, i.e., about 185 mAh g(-1) after 150 cycles at C/5 rate. Also, these cathodes possess higher rate capability as compared to full cells comprising Li1.2Ni0.13Mn0.54Co0.13O2 cathodes. Thus, the electrochemical performance of Li1.2Ni0.27Mn0.40Co0.13O2 cathodes in full cells with prelithiated graphite anodes is promising for practical high energy density Li-ion batteries. These results indicate the positive influence of higher Ni content in Li-and Mn-rich cathodes for better electrochemical performance in practical Li-ion batteries.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据