Additive manufacturing; Direct metal laser sintering (DMLS); Delta phase; Superalloy; IN718
资金
- Grants-in-Aid for Scientific Research [16K06799] Funding Source: KAKEN
The effects of building direction and heat treatment on the tensile properties of superalloy IN718 fabricated by direct metal laser sintering (DMLS) were examined at room temperature and 650 degrees C. It was noted that particle-shaped delta phases were localized in the interdendritic regions due to the segregation of Nb that occurs during the DMLS solidification process. To investigate the microstructure and mechanical properties of DMLS parts, vertical and horizontal specimens were cut parallel and perpendicular to the building direction, respectively. The tensile strengths of heat-treated materials produced by DMLS were comparable to those of cast and wrought specimens; however, when the horizontal-and vertical-direction specimens were subjected to solution treatment and aging (STA) at 650 degrees C, the horizontal-direction specimen exhibited one-fourth the ductility of the vertical-direction specimen because of the interdendritic delta-phase precipitates, which were arrayed perpendicular to the stress axis in the former specimen. The morphology and a row of interdendritic delta-phase precipitates with incoherent interfaces were found to affect tensile ductility at a high temperature. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据