Substructure hardening in duplex low density steel

期刊

MATERIALS & DESIGN
卷 116, 期 -, 页码 472-480

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2016.12.020

关键词

Duplex low density steel; Strain-hardening; Substructure refinement; Subgrain

向作者/读者索取更多资源

The present work was conducted to evaluate the effects of substructure development on the strain hardening behavior of Fe-17.5Mn-83Al-0.74C-0.14Si lightweight steel. This was performed applying tensile testing method at ambient temperature. The significant strain hardening capability of the experimental steel is attributed to the cell structure formation and its progressive evolution to subgrains over a wide range of applied strain. The continuous subgrain refinement with the applied strain could lead to the nano-size partitioning of the austenite (similar to 530 nm) and ferrite (similar to 500 nm) grains. The size of substructure (mesh length) appears to be stabilized at true strains above 0.35, thereby reducing the rate of work hardening and inducing subgrain rotation to higher misorientations. The contribution of substructure refinement is significant and possesses a high portion of the measured flow stress (similar to 550 MPa for austenite and similar to 70 MPa for ferrite at the true strain of 0.5). (C) 2016 Elsevier Ltd. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据