期刊
JOURNAL OF MAGNESIUM AND ALLOYS
卷 4, 期 3, 页码 207-213出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jma.2016.07.004
关键词
Magnesium alloys; Thermomechanical processing; Recrystallization; X-ray diffraction; Mechanical characterization
A new Mg-Al-Sn-RE alloy with high ductility at room temperature has been developed. Homogenized Mg-4Al-2Sn-0.5Y-0.4Nd plates 25 mm in thickness were hot-rolled to 1 mm at 673K. The microstructures were characterized as fully recrystallized grains with a lot of fragmented fine particles along the rolling direction. The sheet specimen possesses basal texture of (0002) with the basal pole tilting by about 15 degrees from the normal direction toward the rolling direction. Meanwhile, the texture strength was weakened, which is resulted from the non-basal slip and recrystallization texture. For the as-rolled alloy, the yield strength and tensile strength in transverse direction are both higher than those of rolling direction. The average Lankford value is 1.83, which is lower than conventional AZ31 rolled magnesium alloy sheets. The relatively high elongation and low planar anisotropy implies good formability at room temperature. (C) 2016 Production and hosting by Elsevier B.V. on behalf of Chongqing University. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据