alloy 2024; alloy 2198; tension; artificial ageing; exfoliation corrosion; ductility
The present work investigates the corrosion resistance of the innovative Al-Cu-Li (2198) aluminum alloy; a comparison against Al-Cu (2024) alloy is attempted. Tensile specimens were pre-corroded for different exposure times to exfoliation corrosion solution and immediately afterwards they were tested in tension. For small exposure times (< 12 h) small pits could be found on the corroded surfaces; pitting was also noticed at the small side surfaces (thickness) of the tensile specimens. Corrosion exposure seems not to essentially decrease the yield stress of AA2198 even for high exposure times, while this was not the case for AA2024. After heavy corrosion exposure (> 12 h), AA2024 lost almost 30% of its initial ultimate tensile strength, while for AA2198 the respective value was only I11%. Al-Cu-Li alloy shows superior corrosion resistance in terms of maintaining higher percentages of tensile ductility; AA2198 exhibited higher remaining elongation at fracture values due to corrosion degradation for all investigated exposure times. Copyright (C) 2016 The Authors. Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据