期刊
BONE RESEARCH
卷 5, 期 -, 页码 -出版社
NATURE PUBLISHING GROUP
DOI: 10.1038/boneres.2017.18
关键词
-
资金
- National Natural Science Foundation of China [81671031, 81470721, 31600778]
- Sichuan Science and Technology Innovation Team [2014TD0001]
Cartilage tissue engineering based on biomimetic scaffolds has become a rapidly developing strategy for repairing cartilage defects. In this study, a biphasic CAN-PAC hydrogel for osteochondral defect (OCD) regeneration was fabricated based on the density difference between the two layers via a thermally reactive, rapid cross-linking method. The upper hydrogel was cross-linked by CSMA and NIPAm, and the lower hydrogel was composed of PECDA, AAm and PEGDA. The interface between the two layers was first grafted by the physical cross-linking of calcium gluconate and alginate, followed by the chemical cross-linking of the carbon-carbon double bonds in the other components. The pore sizes of the upper and lower hydrogels were similar to 187.4 and similar to 112.6 mu m, respectively. The moduli of the upper and lower hydrogels were similar to 0.065 and similar to 0.261 MPa. This prepared bilayer hydrogel exhibited the characteristics of mimetic composition, mimetic structure and mimetic stiffness, which provided a microenvironment for sustaining cell attachment and viability. Meanwhile, the biodegradability and biocompatibility of the CAN-PAC hydrogel were examined in vivo. Furthermore, an osteochondral defect model was developed in rabbits, and the bilayer hydrogels were implanted into the defect. The regenerated tissues in the bilayer hydrogel group exhibited new translucent cartilage and repaired subchondral bone, indicating that the hydrogel can enhance the repair of osteochondral defects.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据