The fabrication of luminescent defects in single-crystal diamond upon Sn implantation and annealing is reported. The relevant spectral features of the optical centers (emission peaks at 593.5, 620.3, 630.7, and 646.7 nm) are attributed to Sn-related defects through the correlation of their photoluminescence (PL) intensity with the implantation fluence. Single Sn-related defects were identified and characterized through the acquisition of their second-order autocorrelation emission functions, by means of Hanbury-Brown and Twiss interferometry. The investigation of their single-photon emission regime as a function of excitation laser power revealed that Sn-related defects are based on three-level systems with a 6 ns radiative decay lifetime. In a fraction of the studied centers, the observation of a blinking PL emission is indicative of the existence of a dark state. Furthermore, absorption dependence on the polarization of the excitation radiation with similar to 45% contrast was measured. This work shed light on the existence of a new optical center associated with a group-IV impurity in diamond, with similar photophysical properties to the already well-known Si-V and Ge-V emitters, thus, providing results of interest from both the fundamental and applicative points of view.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据