PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL
卷 27, 期 6, 页码 695-702出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.pnsc.2017.11.002
关键词
Magnesium alloys; Sn addition; Microstructure; Texture; Mechanical properties
资金
- National Natural Science Foundation of China [51531002, 51474043]
- Ministry of Education of China [SRFDR 20130191110018]
- Chongqing Municipal Government [CSTC2013JCYJC60001]
The effects of Sn addition (0, 0.5, 1.0, 2.0 and 3 wt%) on microstructure of Mg-4Zn-1.5Al alloy in cast and extruded states were investigated, and the mechanical properties of as-extruded Mg-4Zn-1.5Al-xSn studied. The experimental results showed that the as-cast Mg-4Zn-1.5Al alloy was composed of two phases alpha-Mg and Mg-32 (Al, Zn) 49, while Sn-containing alloys consisted of a-Mg, Mg-32 (Al, Zn) 49 and Mg2Sn phases, and Mg-32 (Al, Zn) 49 was not detected after extruding due to that the most of them dissolved into the matrix during the homogenized treatment. The addition of Sn refined the grains of as-cast and as-extruded Mg-Zn-Al alloys obviously. It was noted that the basal texture intensity reduced with increasing Sn content significantly in as-extruded Mg-Zn-Al alloys. The tensile tests results indicated that Sn addition improve the tensile strength of the extruded alloys, while it had a harmful effect on the ductility. When the addition of Sn was 2 wt%, the ultimate tensile strength (UTS), yield strength (YS) and elongation (epsilon(f)) of the alloy were 280 MPa, 147 MPa and 17.4%, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据