CORROSION SCIENCE
卷 114, 期 -, 页码 156-168出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2016.11.013
关键词
Aluminum alloys; TEM; SEM; Intergranular corrosion; Pitting corrosion
The intergranular corrosion (IGC) susceptibility of 2024 Al alloy during re-ageing after solution treating and cold-rolling was investigated by accelerated corrosion testing, open circuit potential testing, transmission electron microscopy and scanning electron microscopy. The absence of IGC in both the peak-re-aged and over-re-aged samples is related to the dislocation pile-ups which prevent the supersaturated solutes from diffusing into the grain boundaries and precipitating the continuous S-AL(2)CuMg phase. The aggregated pitting corrosion in the over-re-aged samples arises from the S-phase precipitates on the dislocation cell walls which accelerate the anodic dissolution of the cell interiors. (C) 2016 Elsevier Ltd. All rights reserved.