CERAMICS INTERNATIONAL
卷 43, 期 2, 页码 2170-2173出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2016.10.200
关键词
Composites; Mechanical properties; Structural applications
资金
- National Natural Science Foundation of China [11502058]
- Heilongjiang Postdoctoral Science Foundation Funded Project [LBH-Z15071]
- Aerospace Innovation Fund [BAQQ2440900316]
HfB2-x vol%CNTs (x=0, 5, 10, and 15) composites are prepared by spark plasma sintering. The influence of CNTs content and sintering temperature on densification, microstructure and mechanical properties is studied. Compared with pure HfB2 ceramic, the sinterability of HfB2-CNTs composites is remarkably improved by the addition of CNTs. Appropriate addition of CNTs (10 vol%) and sintering temperature (1800 degrees C) can achieve the highest mechanical properties: the hardness, flexural strength and fracture toughness are measured to be 21.8 +/- 0.5 GPa, 894 +/- 60 MPa, and 7.8 +/- 0.2 MPa m(1/2), respectively. This is contributed to the optimal combination of the relative density, grain size and the dispersion of CNTs. The crack deflection, CNTs debonding and pull-out are observed and supposed to exhaust more fracture energy during the fracture process.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据