CERAMICS INTERNATIONAL
卷 43, 期 2, 页码 1716-1721出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2016.08.144
关键词
Perovskite; Solid electrolyte; Ionic conductivity; Ion doping
资金
- National Natural Science Foundation of China [51372012]
Perovskite-type structured solid electrolytes with the general formula (Li0.25La0.25)(1-x)M0.5xNbO3 (M=Sr, Ba, Ca, x=0.125) have been prepared by solid-state reaction. Their crystal structure and ionic conductivity were examined by means of X-ray diffraction analysis (XRD), scanning electron microscope (SEM), and alternating current (AC) impedance technique. All sintered compounds are isostructural with the parent compound Li0.5La0.5Nb2O6. Some impurity phase is detected at the grain boundary in the Ba- and Ca-substituted compounds. The substitution of partial Li+ by alkaline earth metal ions has responsibility for the cell volume expansion as determined by the XRD data. The densification is accelerated, with the overall porosity and grain boundary minimized as Sr2+ ions are doped. Among the investigated compounds, the perovskite (Li0.25La0.25)(0.875)Sr0.0625NbO3 shows a remarkable ionic conductivity of 1.02x10(-5) S/cm at room temperature (20 degrees C) and the lowest activation energy of 0.34 eV in comparison with 0.38 eV and 0.44 eV for the corresponding Ba- and Ca-doped samples, respectively. It is identified that the enhancement of ionic conductivity is attributed to a reduction in activation energy for ionic conduction which is related to an increase in the cell volume.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据