期刊
CERAMICS INTERNATIONAL
卷 43, 期 1, 页码 1180-1185出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2016.10.060
关键词
Hexaferrites; Ferromagnetism; Dielectrics; Magneto-electrics
资金
- Council of Scientific and Industrial Research (C.S.I.R.), New Delhi [03(1370)/16/EMR-II]
Pb-substituted barium hexaferrite with chemical formula, Ba1-xPbxFe12O19 (x=0.0, 0.1, 0.2, 0.3, 0.4) were prepared by co-precipitation method and citric acid was used as the organic precipitating agent. The samples were characterized by X-ray (XRD), scanning electron microscopy (SEM), Polarization versus Electric field (PE) loop tracers and vibrating sample magnetometer (VSM). XRD analysis confirms the single hexagonal phase formation for all the compounds and indicates that all Pb ions are situated into the lattice of barium ferrite. Images of scanning electron microscopy show that the grains are regular and well defined structures. P-E loops shows that the value of remnant polarization and saturation polarization increases up to x=0.2 and then decreases with increasing the Pb doping contents. Magnetization versus field (M-H) curves shows that the coercivity first increases and then decreases with the increase in Pb content with maximum value of coercivity (1270.38 Gauss) for x=0.2 sample. Magnetoelectric quadratic coefficient beta has been measured by the dynamic magnetoelectric method at room temperature. The maximum value of magneto-electric coupling coefficient is 5.27x10(-4) mu V/cm-Oe(2) at 3500 Oe for x=0.3 sample.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据