BIOMEDICAL MICRODEVICES
卷 19, 期 1, 页码 -出版社
SPRINGER
DOI: 10.1007/s10544-016-0144-1
关键词
Transdermal drug delivery; Coated-microneedles; Local anesthesia; Lidocaine; Poly (L-lactide)
资金
- Ministry of Science, ICT, and Future Planning [NRF-2014M3A9E4064580]
- Advanced Biomass R & D Center (ABC) of the Global Frontier Project - Ministry of Science, ICT, and Future Planning [ABC-2011-0031350]
This study showed that drug-coated PLLA (Poly (L-lactide)) microneedle arrays can induce rapid and painless local anesthesia. Microneedle arrays were fabricated using a micro-molding technique, and the needle tips were coated with 290.6 +/- 45.9 mu g of lidocaine, the most widely used local anesthetic worldwide. A dip-coating device was newly designed for the coating step using an optimized coating formulation. Lidocaine coated on the arrays was released rapidly into PBS within 2 min, and its stability in storage lasted 3 weeks at 4, 25, and 37 degrees C. Furthermore, the microneedle arrays showed consistent in vitro skin penetration and delivered 200.8 +/- 43.9, 224.2 +/- 39.3, and 244.1 +/- 19.6 mu g of lidocaine into the skin 1, 2, and 5 min after application with a high delivery efficiency of 69, 77, and 84%. Compared to a commercially available topical anesthetic EMLA (R) cream, a 22.0, 13.6, and 14.0-fold higher amount of lidocaine was delivered into the skin. Note, in vitro skin permeation of Lidocaine was also notably enhanced by a 2-minapplication of the lidocaine-coated microneedle arrays. Altogether, these results suggest that the biocompatible lidocaine-coated PLLA microneedle arrays could provide significantly rapid local anesthesia in a painless manner without any of the issues from topical applications or hypodermic injections of local anesthetics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据