ELECTROCHIMICA ACTA
卷 225, 期 -, 页码 235-242出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2016.12.121
关键词
prussian blue; cathode; sodium ion batteries
资金
- Natural Science Foundation of China [21573147, 21506123, 21336003]
- Major Basic Research Program of China [2014CB239703, 2016YFB0901505]
- Science and Technology Commission of Shanghai Municipality [15ZR1422300]
Prussian blue and its analogues have been intensively studied as potential electrode materials for sodium ion batteries. In this work, a prussian blue sample was prepared by a simple precipitation method and the electrochemical performance of the prussian blue (PB) cathode was investigated at various temperatures and in different voltage ranges. When cycled in the voltage range of 2.0 - 4.0 V vs. Na/Na+, the PB cathode exhibited initial discharge capacities of 135.4 mAh g(-1) (55 degrees C), 128.5 mAh g(-1) (25 degrees C) and 99.2 mAh g(-1) (- 10 degrees C) at 10 mA g(-1). The PB cathode showed good cycling stability at low temperature, however the cycling capacity degraded remarkably at elevated temperature. CV test indicated that the capacity fade was mainly due to the side reactions on the electrode-electrolyte interface at near 4.0 V vs. Na/Na+. XPS and FTIR analyses revealed several types of compounds formed on the cathode surface which indicated the complexity of the side reactions. Controlling the high cut-off voltage at 3.8 V vs. Na/Na+ significantly improved the cycling stability of the PB electrode. The PB cathode delivered 1C rate reversible capacity of 100.0 mAh g(-1) in 2.0 - 3.8 V vs. Na/Na+ with outstanding capacity retention of 98.2% after 300 cycles. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据