期刊
CONSTRUCTION AND BUILDING MATERIALS
卷 133, 期 -, 页码 57-64出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2016.12.034
关键词
Multi-walled carbon nanotube; Mortar-aggregate interface; Tensile strength; Shear strength; Industrial grade
资金
- National Basic Research Program of China (973 Program) [2015CB057703]
This paper presents the test results of the mortar-aggregate interfacial strength properties considering six dosages of industrial grade pre-dispersed multi-walled carbon nanotube paste. Mechanical and ultrasonication dispersion were carried out and scanning electron microscope was taken for dispersion inspection. The test results indicated a stable yet negative effect of carbon nanotube paste on the mortar compression strength; while a widely scattered (coefficient of variation up to 23.6%) positive effect on the interfacial tensile strength (maximum 8.4% increase at 0.2 wt% carbon nanotube) was observed. It was also found that the increase of the interfacial shear strength was much more significant (maximum 51.5% at 0.05 wt% carbon nanotube) with a medium variation. Analysis of the mortar strength, interfacial tensile strength and shear strength showed no solid correlation amongst the three strength properties, which implies that the reinforcing mechanism of the carbon nanotube to the mortar-aggregate interface along various directions can be substantially different. The generated knowledge will be incorporated in a meso-scale analysis of carbon nanotube reinforced concrete, in which the aggregate, mortar and interface will be considered separately. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据