The present study was performed on Mg-based alloys containing Zn and Mn. The alloys were cast in a permanent metallic mold preheated to 200 degrees C and with a protective atmosphere of dry air, CO2, and SF6. Two main phases are observed in the as-cast condition: Mg-Al-Zn and Mn-Al intermetallics. The size and morphology of the Mg-Al-Zn phase are significantly affected by the concentration of Al. Tensile properties, using standard ASTM B-108 samples, are directly related to the size, morphology, and density of the existing phase particles. The alloy ductility is reduced with increase in the Al concentration, whereas the ultimate tensile strength and the yield strength are more or less stable. The fracture surface of the tested tensile bars is mostly ductile for low Al-containing alloys and tends to be brittle with the increase in Al content as evidenced by an increase in the density of cleavage ruptured areas.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据