ADVANCES IN MATERIALS SCIENCE AND ENGINEERING
卷 2017, 期 -, 页码 -出版社
HINDAWI LTD
DOI: 10.1155/2017/4065434
关键词
-
A cast Mg-8Al-1Zn-1Ca magnesium alloy was multipass hot rolled at different sample and roll temperatures. The effect of the rolling conditions and reduction in thickness on the microstructure and mechanical properties was investigated. The optimal combination of the ultimate tensile strength, 351 MPa, yield strength, 304 MPa, and ductility, 12.2%, was obtained with the 3 mm thick Mg-8Al-1Zn-1Ca rolled sheet, which was produced with a roll temperature of 80 degrees C and sample temperature of 430 degrees C. This rolling process resulted in the formation of a bimodal structure in the alpha-Mg matrix, which consequently led to good ductility and high strength, exclusively by the hot rolling process. The 3 mm thick rolled sheet exhibited fine (mean grain size of 2.7 mu m) and coarse grain regions (mean grain size of 13.6 mu m) with area fractions of 29% and 71%, respectively. In summary, the balance between the strength and ductility was enhanced by the grain refinement of the alpha-Mg matrix and by controlling the frequency and orientation of the grains.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据