APPLIED SURFACE SCIENCE
卷 399, 期 -, 页码 114-122出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.apsusc.2016.12.066
关键词
Three-dimensionally ordered macroporous; La0.8Ce0.2FeO3 perovskite; K-Mn composite oxide; Soot removal
类别
资金
- National Key Research and Development Program of China [2016YFC0204301]
- R&D Project for Environmental Protection of Jiangsu of China [2015002]
- Opening Foundation of Jiangsu Key Laboratory of Vehicle Emissions Control [OVEC031]
Three-dimensionally ordered macroporous (3DOM) La0.8Ce0.2FeO3 perovskite was successfully constructed through a colloidal crystal template way. And the K-Mn/3DOM La0.8Ce0.2FeO3 catalyst was obtained by an incipient-wetness impregnation method. The physicochemical characterizations of the material were conducted by means of XRD, FESEM, TEM, N-2 adsorption-desorption, H-2-TPR, XPS and O-2-TPD techniques, and the catalytic performance was evaluated for soot removal. The intact well-ordered macroporous skeleton was remained after K and Mn were loaded, which offered an ideal environment for soot combustion. The generated K2Mn4O8 was well decorated on the skeleton of the 3DOM perovskite, which could increase the concentration of surface oxygen species and enhance the reducibility of catalyst. The as-prepared catalyst exhibited good catalytic performance for soot removal, and could lower the T-50 of soot to 377 degrees C. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据