Lithium metal batteries (LMBs) containing S, O-2, and fluoride cathodes are attracting increasing attention owing to their much higher energy density than that of Li-ion batteries. However, current limitation for the progress of LMBs mainly comes from the uncontrolled formation and growth of Li dendrites at the anode side. In order to suppress dendrite growth, exploring novel nanostructured electrolyte of high modulus without degradation of Li-electrolyte interface appears to be a potential solution. Here we propose a lightweight polymer-reinforced electrolyte based on graphitic carbon nitride (g-C3N4) mesoporous microspheres as electrolyte filler [bis(trifluoromethanesulfonimide) lithium salt/di(ethylene glycol) dimethyl ether mixed with g-C3N4, denoted as LiTFSI-DGM-C3N4] for the first time. This nanostructured electrolyte can effectively suppress lithium dendrite growth during cycling, benefiting from the high mechanical strength and nanosheet-built hierarchical structure of g-C3N4. The Li/Li symmetrical cell based on this slurrylike electrolyte enables long-term cycling of at least 120 cycles with a high capacity of 6 mA center dot h/cm(2) and small plating/stripping overpotential of similar to 100 mV at a high current density of 2 mA/cm(2). g-C3N4 filling also enables a separator(Celgard)-free Li/FeS2 cell with at least 400 cycles. The 3D geometry of g-C3N4 shows advantages on interfacial resistance and Li plating/stripping stability compared to its 2D geometry.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据