CERAMICS INTERNATIONAL
卷 43, 期 6, 页码 4910-4918出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2016.12.142
关键词
Porous ceramics; Lead-zinc mine tailing; Waste; Anorthite
资金
- National Natural Science Foundation of China [51502349]
- Nonferrous Metals Foundation of Hunan in China [YSZN2013CX02]
The porous ceramics were prepared by directly sintering of lead-zinc mine tailings and fly ash as the raw materials without any additional sintering and foaming agent. The effects of fly ash addition on the crystalline phases, pore structure, physical chemical porosities and mechanical strength were investigated. The results showed that the bulk density decreased firstly and then increased while the porosity and water absorption presented the opposite tendency with the increase of fly ash content. Meanwhile, the chemical stability improved and the flexural strength had the same variation tendency of the bulk density. The phase evolution of sample with 60 wt% fly ash addition indicated that anorthite phase was formed at low temperature (1000 degrees C). The thermal behavior illustrated that the foaming process was initiated by the reaction of internal constituents in the lead-zinc mine tailings. Different pore structures indicated different foaming mechanisms that probably occurred at different temperatures. The porous ceramics with 60 wt% fly ash addition exhibited excellent properties, including bulk density of 0.93 g/cm(3), porosity of 65.6%, and flexural strength of 11.9 MPa.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据