Nanoporous carbon decorated with Fe nanoparticles (Fe/C) was prepared via in situ carbonization of Fe precursor-encapsulated Zn-based metal organic framework (ZIF8). In the synthetic process, iron precursor (ferrous salt) was mechanically mixed with pre-synthesized ZIF8 taking advantage of the porous characteristic of ZIF8, and then converted to Fe nanoparticles (NPs) at high temperature. The Fe NPs with low content and small size were uniformly embedded in porous graphitic carbon matrix. When the filler loading of Fe/C composite is as low as 15 wt% in paraffin matrix, the absorber exhibited a minimum reflection loss of -29.5 dB at a thickness of 2.5 mm, The strong absorbing capability together with the lightweight feature is closely associated with the well-designed constituent and structure of the composite, which result in good impedance matching and strong electromagnetic energy loss due to the dual-loss mechanism and the synergistic effect between Fe NPs and carbon matrix. This study not only provides a lightweight electromagnetic wave absorbing material, but also offers a general way to prepare metal NPs-nanoporous carbon composite absorber. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据