期刊
CURRENT APPLIED PHYSICS
卷 17, 期 4, 页码 501-506出版社
ELSEVIER
DOI: 10.1016/j.cap.2017.01.020
关键词
Solvothermal process; Nickel cobalt hydroxide; Nanofoam structure; Electrochemical properties
资金
- National research Foundation of Korea [2015M2A2A6A02045252, 2015R1D1A1A01058851, 2015R1D1A1A01060743, 2015R1A2A2A01004782, 2016R1A6A1A03012877]
- Dongguk University research fund
- National Research Foundation of Korea [2015M2A2A6A02045252, 2015R1D1A1A01060743, 2015R1D1A1A01058851, 2015R1A2A2A01004782] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
A nanofoam nickel cobalt layered double hydroxide (NiCo(OH)(2)) electrode film is fabricated on a stainless-steel substrate with the use of a simple one-step solvothermal process. The nanofoam NiCo(OH)(2) electrode exhibits a high specific capacitance of 2710.2 Fig at a current density.of 9.1 A/g, and a good capacity retention of similar to 70% after 2000 charge-discharge cycles at a high current density of 31.8 A/g. An energy density of 60.23 Wh/kg is obtained at a power density of 1.8 kW/kg. The excellent electrochemical energy storage performance of the NiCo(OH)(2) electrode is due to the synergetic effect of a significantly improved ionic diffusion and an effective charge transfer, which is linked to a well-dispersed interconnected nanofoam morphology and binder-free direct contact with the current collector. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据