JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
卷 125, 期 4, 页码 223-226出版社
CERAMIC SOC JAPAN-NIPPON SERAMIKKUSU KYOKAI
DOI: 10.2109/jcersj2.16251
关键词
Perovskite; Solid oxide fuel cell; Phase stability; A-site deficiency
Nb-substituted or Ta-substituted strontium titanates were synthesized by conventional solid-state reactions. For perovskite-type titanates, Sr1-yTi1-xMxO3, the lattice constant a was found to increase with the amount of dopant (x) added, to maximum values of 3.927 and 3.930 (A) over circle for M = Nb and Ta respectively, regardless of Sr deficiency (y). X-ray diffraction studies revealed that the Ta-substituted strontium titanate possesses a wider stable region in its perovskite-type structure against the amount of added dopant (x) and strontium deficiency (y), compared with the Nb-substituted structure. Even in the single phase regions of SrTi1-xMxO3 (M = Nb and Ta) perovskites, scanning electron microscopy images confirmed that after firing at 1500 degrees C for 10 h some SrTi0.9Ta0.1O3 grains showed strontium and tantalum enrichment and titanium dilution, whereas no inhomogeneity was found in SrTi0.9Nb0.1O3. This cationic compositional fluctuation is consistent with the lower electrical conductivity of SrTi0.9Ta0.1O3 compared with SrTi0.9Nb0.1O3 at low temperatures. (C) 2017 The Ceramic Society of Japan. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据