期刊
CORROSION SCIENCE
卷 120, 期 -, 页码 194-210出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2016.12.007
关键词
Stainless steel; Polarization; TEM; Pitting corrosion; Thermodynamic diagrams; welding
资金
- National Natural Science Foundation of China [51575382]
- Marine Economic Innovation and Development of Regional Demonstration Projects of China [cxsf2014-12]
The influence of microstructural evolution on selective corrosion in duplex stainless steel flux-cored arc welding joint was investigated by the modified double loop electrochemical potentiokinetic reactivation in acidified chloride. Due to the lower pitting resistance equivalent number, the secondary austenite was preferentially attacked over the ferrite and primary austenite phases, and inclusions acted as nucleation sites for micro-pits in the weld metal. Localised corrosion was generated in the secondary austenite and Cr-depleted zone around the Cr2N and sigma phases in the heat-affected zone. The weld metal exhibited the smallest susceptibility to localised corrosion because of the least weak phases. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据