NH3-SCR; Ca poisoned; Resistance; Adsorbed NO2; Acid sites
资金
- National Natural Science Foundation of China [21325731, 21407088, 51478241]
- National High-Tech Research and Development (863) Program of China [2013AA065401]
- China Postdoctoral Science Foundation [2013M530643]
The SCR performances of CaO poisoning CeO2-WO3 and V2O5-WO3/TiO2 catalysts were prepared and compared for selective catalytic reduction of NO with NH3 (NH3-SCR). It was found that the CeO2-WO3 catalyst showed better calcium resistance than V2O5-WO3/TiO2 catalyst even when the CaO mass percentage reached up to 5 wt%. In order to further understand the resistance mechanism, XRD, Raman, XPS, H-2-TPR, NH3-TPD and in situ DRIFTS were used to analyze and explore the changes of CeO2-WO3 catalysts before and after the CaO deactivation. The results manifested that the introduction of Ca species not only affected CeO2 lattice but also led to CaWO4 formation on the surface. Additionally, although CaO increased the surface chemisorbed oxygen and Ce4+ species, the reducibility and Lewis acid sites, NH3 chemisorbed amount and Bronsted acid sites were greatly inhibited after deactivation. Furthermore, the enhanced NO2 adsorption capacity after the alkaline Ca species introduction could partially offset the negative effect in the loss of acid sites over the catalyst surface, which might be the primary reason for stronger CaO resistance of CW catalyst than traditional V2O5-WO3/TiO2 catalyst. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据