ACTA BIOMATERIALIA
卷 55, 期 -, 页码 323-332出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.actbio.2017.04.001
关键词
Fast scanning calorimetry; Silk I; Silk II; Wide angle X-ray scattering; Fourier transform infrared (FTIR)
资金
- National Science Foundation, Polymers Program of the Division of Materials Research [DMR-1206021, DMR-1608125]
- DAAD
- Department of Defense (DOD) through the National Defense Science & Engineering Graduate Fellowship (NDSEG) program
- Division Of Materials Research
- Direct For Mathematical & Physical Scien [1608125] Funding Source: National Science Foundation
Using fast scanning calorimetry (FSC), we investigated the glass transition and crystal melting of samples of B. mori silk fibroin containing Silk I and/or Silk II crystals. Due to the very short residence times at high temperatures during such measurements, thermal decomposition of silk protein can be significantly suppressed. FSC was performed at 2000 K/s using the Mettler Flash DSC1 on fibroin films with masses around 130-270 ng. Films were prepared with different crystalline fractions (ranging from 0.26 to 0.50) and with different crystal structures (Silk I, Silk II, or mixed) by varying the processing conditions. These included water annealing at different temperatures, exposure to 50% MeOH in water, or autoclaving. The resulting crystal structure was examined using wide angle X-ray scattering. Degree of crystallinity was evaluated from Fourier transform infrared (FTIR) spectroscopy and from analysis of the heat capacity increment at the glass transition temperature. Silk fibroin films prepared by water annealing at 25 degrees C were the least crystalline and had Silk I structure. FTIR and FSC studies showed that films prepared by autoclaving or 50% MeOH exposure were the most crystalline and had Silk II structure. Intermediate crystalline fraction and mixed Silk I/Silk II structures were found in films prepared by water annealing at 37 degrees C. FSC results indicate that Silk II crystals exhibit endotherms of narrower width and have higher mean melting temperature T-m(II) = 351 +/- 2.6 degrees C, compared to Silk I crystals which melt at T-m(I) = 292 +/- 3.8 degrees C. Films containing mixed Silk I/Silk II structure showed two clearly separated endothermic peaks. Evidence suggests that the two types of crystals melt separately and do not thermally interconvert on the extremely short time scale (0.065 s between onset and end of melting) of the FSC experiment. Statement of Significance Silkworm silk is a naturally occurring biomaterial. The fibroin component of silk forms two types of crystals. Silk properties depend upon the amount and type of crystals, and their stability. One measure of stability is crystal melting temperature. Crystals which are more stable have a higher melting temperature. Until now, it has been challenging to study thermal behavior of silk crystals because they degrade at high temperature. To avoid degradation, and study the melting properties of silk biomaterial, we heated silk at a very fast rate of 2000 K/s using a special calorimeter. We have shown that the two crystal types have very different melting temperatures, indicating that one crystal type is much more stable than the other. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.