期刊
COMPOSITES PART B-ENGINEERING
卷 119, 期 -, 页码 32-40出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesb.2017.03.019
关键词
Polymer-matrix composites (PMCs); Thermosetting resin; Fracture toughness; Fractography
资金
- National Key Research Program of China [2016YFB0302702]
- Scientific Research Fund of Hunan Provincial Education Department [17A126]
- Hunan Engineering Laboratory for Preparation Technology of Polyvinyl Alcohol Fiber Material, Huaihua University [HGY201612]
In this study, a series of adipic acid-polyoxypropylene diamine copolymer (AA-PPA) was prepared by copolymerizing polyoxypropylene diamine (PPA D400) and adipic acid (AA). The AA-PPA with weight average molecular weight (M-w) = 10400 and weight-average molecular weight (M-n) = 7600 was used to modify diglycidyl ether of bisphenol A (DGEBA) epoxy/diethyl toluene diamine (DDM) system. This extended polyether AA-PPA showed unique advantages over traditional polyether at achieving the synchronous enhancement of strength and fracture toughness. With 30 wt% AA-PPA, the bending strength, tensile strength, elongation at break and impact strength were improved by 7.50%, 6.90%, 36.13% and 288.00%, respectively. The single glass transition temperature (T-g) step proved the homogeneous phase structure of modified epoxy resins. Inevitably, the T-g of modified epoxy decreased for the addition of soft segments. The dynamic mechanical analysis (DMA) results indicated that the storage modulus of modified epoxy increased with the increasing content or AA-PPA, while the loss modulus decreased. The interaction of the crosslinked network was explained by calculating the theoretical and measured values of the molecular weight between the crosslinks. The morphology showing the ductile fracture of modified epoxy was testified by scanning electron microscopy (SEM). (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据