卷 43, 期 11, 页码 8126-8132出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2017.03.136
关键词
Brazing; Network structure; Microstructure; Residual stress; Mechanical properties
资金
- National Natural Science Foundation of China [51522404, 51321061]
A novel composite interlayer with a reinforced network was designed using a SiC ceramic with a network structure and Ti-Ni-Nb composite filler foils, to which the Nb and BN-Sio(2) ceramic were successfully brazed under vacuum. For a brazing temperature of 1160 degrees C and holding time of 10 min, the interfacial microstructure of the Nb/BN-Sio(2) ceramic joint was Nb/((beta Ti,Nb)-TiNi eutectic structure+((beta Ti,Nb)(2)Ni+SiC+TiC/TiN+Ti2N +TiB+Ti5Si3+TiO/BN-SiO2 ceramic. In addition, the shear strength and nano-hardness were analyzed to evaluate the effect of the composite interlayer with a network reinforcement architecture on the mechanical properties of the joint. During brazing, the Ti-Ni-Nb filler metal infiltrated and reacted with the SiC to form the network reinforcement architecture, resulting in the residual stress being relieved and the mechanical performance of the joint being significantly improved. A maximum shear strength of 102 MPa was achieved, which was 60 MPa (142%) higher than that of the joint brazed without the network reinforcement architecture. A reduction in the residual stress on the BN-SiO2 ceramic side from 328 MPa to 210 MPa was observed with the network reinforcement architecture, and the fracture path of the joint changed from the surface of the BN-SiO2 ceramic to the interfacial reaction zone.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据