CONSTRUCTION AND BUILDING MATERIALS
卷 145, 期 -, 页码 52-61出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2017.03.176
关键词
Porosity; Pore volume distribution; SCMs; Cement paste; Accelerated carbonation
资金
- China Scholarship Council (CSC)
Supplementary cementitious materials (SCMs) like fly ash (FA) and blast furnace slag (BFS) are normally used to replace parts of Ordinary Portland cement (OPC) to reduce the cost and CO2 emission. During the carbonation, a relatively high amount of C-S-H with low Ca/Si ratio will be carbonated in cement paste blended with SCMs. Therefore, it's very important to figure out the influences of the carbonation of C-S-H on the pore structure of SCMs blended cement paste. In this paper, Mercury Intrusion Porosimetry (MIP) are used to determine the pore volume and size distribution of capillary pores. Results reveal that carbonation of most of the species of C-S-H results in increased porosity of cement paste. Total and effective capillary porosity of pastes blended with high amount of BFS increase after carbonation. This will bring adverse effects on the durability of blended cement concrete exposed to the carbonation. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据