期刊
COMPOSITES PART B-ENGINEERING
卷 120, 期 -, 页码 97-102出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesb.2017.03.055
关键词
Polymer-matrix composites (PMCs); Particle-reinforcement; Electrical properties; Magnetic properties; Microstructures
资金
- Portuguese Fundacao para a Ciencia e Tecnologia (FCT) [UID/FIS/04650/2013, PTDC/EEI-SII/5582/2014]
- FCT [SFRH/BPD/96227/2013]
- Spanish Ministry of Economy and Competitiveness (MINECO) [MAT2016-76039-C4-3-R]
- FEDER
- Basque Government Industry Department under the ELKARTEK Program
- Fundação para a Ciência e a Tecnologia [UID/FIS/04650/2013, PTDC/EEI-SII/5582/2014] Funding Source: FCT
Magnetoelectric (ME) particulate composites films composed of Terfenol-D (TD) particles embedded in P(VDF-TrFE) (70/30) polymer have been developed. The effect of TD content on the mechanical, dielectric, electric, magnetic, piezoelectric and ME properties was studied and discussed. It is shown that the addition of TD particles into the polymer matrix increased the Young's modulus of from 0.86 GPa from the pristine co-polymer to 0.96 GPa for the composite with 60 wt.% filler content. The dielectric characterization showed an increase of the permittivity and dielectric loss with increasing filler content, being maximized for sample with 60 wt.% of TD (13 and 0.05 respectively). The poling process optimized the d(33) piezoelectric response of the composites to approximate to -15 pC.N-1 value. The room temperature ferro-magnetism (150 Oe coercivity and 8.6 emu.g(-1) saturation magnetization) and high magnetoelectric voltage coupling (38 mV cm(-1).Oe(-1)), the highest reported for two phase TD polymer composites, allows the development of flexible ME devices. (C) 2017 Elsevier Ltd. All rights reserved.