BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO
卷 56, 期 3, 页码 139-145出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.bsecv.2017.03.002
关键词
Sol-gel; Silica nanoparticles; Mesoporous
资金
- MINECO [PTQ-13-05985]
- [S2013/MIT-2862]
- [MAT2015-70780-C4-1]
Development of mesoporous silica nanoparticles as carriers for drug delivery systems has increased exponentially during the last decade. The present work is focused on the synthesis of silica carriers by sol-gel from tetraethyl orthosilicate (TEOS) as precursor of silica and cetyltrimethylammonium bromide ( CTAB) as pore generating agent. The synthesis conditions were modified varying the molar ratio of water/TEOS, NH3/TEOS and amount of CTAB. The silica particles were characterized by scan electron microscopy techniques (FESEM), high resolution transmission electron microscopy (HR-TEM), N-2 adsorption-desorption isotherms, Zeta-potential and Dynamic Light Scattering (DLS). The results show that the specific surface area and the porosity of silica particles were strongly affected by the addition of CTAB and the amount of H2O. The dispersion and stability of silica mesoporous particlesis achieved in spite of the high surface reactivity. The synthesis formulation affects considerably to the particle morphology, which changes from spheres to rods when the molar ratio of H2O increases. A maximum specific surface area of 1480m(2)/g was obtained with pore sizes ranging 2.5-2.8 nm. (c) 2017 SECV. Published by Elsevier Espana, S.L.U.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据