Contact resistance; failure mechanisms; fretting; fretting corrosion; fretting wear
Using an electrodynamic-shaker-based test setup, experiments were performed on gold-plated contacts under a variety of fretting conditions, including different vibration frequencies, vibration amplitudes, and different environment temperatures. The variations in contact resistance with fretting cycles are recorded explicitly. The fretted surface is examined using a scanning electron microscope, energy-dispersive X-ray spectroscopy, and a con-focal laser scanning microscope to assess the surface morphology, extent of oxidation, and elemental distribution across the fretted zone. It was found that fretting damage is a complex phenomenon for electrical contact applications. Different fretting regimes, including the robust electrical contact performance, the oxidation-dominated failure, and the transient unstable conductivity failure are determined. Finally, the degradation mechanisms of gold-plated contacts are proposed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据