ACS APPLIED MATERIALS & INTERFACES
卷 9, 期 28, 页码 23949-23956出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.7b05377
关键词
vanadium pentoxide; 2D material; anisotropy; transport; Raman
资金
- Air Force Office of Scientific Research (AFOSR) [FA 9550-12-1-0441]
- NSF CAREER Grant [DMR-1552482]
- RUI Grant [DMR-1410496]
- UNI Faculty Summer Fellowship
- Division Of Materials Research
- Direct For Mathematical & Physical Scien [1410496, 1760668] Funding Source: National Science Foundation
V2O5 with a layered van der Waals (vdW) structure has been widely studied because of the material's potential in applications such as battery electrodes. In this work, microelectronic devices were fabricated to study the electrical and optical properties of mechanically exfoliated multilayered V2O5 flakes. Raman spectroscopy was used to determine the crystal structure axes of the nanciflakes and revealed that the intensities of the Raman modes depend strongly on the relative orientation between the crystal axes and the polarization directions of incident/scattered light. Angular dependence of four-probe resistance measured in the van der Pauw (vdP) configuration revealed an in-plane anisotropic resistance ratio of similar to 100 between the a and b crystal axes, the largest in-plane transport anisotropy effect experiMentally reported for two-dimensional (2D) materials to date. This very large resistance anisotropic ratio is explained by the nonuniform current flow in the vdP measurement and an intrinsic mobility anisotropy ratio of 10 between the a and b crystal axes. Room-temperature electron Hall mobility up to 7 cm(2)/(V s) along the high-mobility direction was obtained. This work demonstrates V2O5 as a layered 2D vdW oxide material with strongly anisotropic optical and electronic properties for novel applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据