期刊
CATALYSIS SCIENCE & TECHNOLOGY
卷 7, 期 15, 页码 3312-3324出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c7cy00708f
关键词
-
资金
- National Natural Science Foundation of China [21276253]
- Talent Scientific Research Fund of LSHU [2013XJJ-018]
Highly dispersed beta-Mo2C and alpha-MoC1-x nanoparticles with average diameters of 3.88 +/- 1.21 and 1.79 +/- 0.72 nm, respectively, were synthesized by a simple resin-based carbothermal reduction route. It was interesting to note that the nature of the Mo carbide phases obtained considerably depended on the precursor preparation method and flowing gas composition. Under flowing Ar gas, the precursors prepared by ion-exchange, impregnation and mechanical mixture methods were transformed into alpha-MoC1-x, a alpha-MoC1-x/ beta-Mo2C mixture and beta-Mo2C, respectively. However, under flowing H-2 gas, all the precursors were converted to beta-Mo2C, regardless of the precursor preparation method. The complete synthesis processes involved reduction-carburization of Mo oxide precursors via the pathways of nontopotactic MoO2 -> beta-Mo2C or MoOx (Mo4+ or/and Mo5+). MoOxCy -> beta-Mo2C, and topotactic MoOx(Mo5+) -> MoOxCy -> alpha-MoC1-x. It was generally accepted that there were two possible mechanisms of dry reforming of methane (DRM) on beta-Mo2C, the redox mechanism (involving beta-Mo2C reversible arrow MoO2) and the noble metal type mechanism, with the former much more dominant than the latter. In this work, we addressed for the first time the differences in the two mechanisms between beta-Mo2C and alpha-MoC1-x. Over the a-phase, the redox mechanism involved the transformation of alpha-MoC1-x -> MoO2 reversible arrow beta-Mo2C and this pathway was minor in comparison to the noble metal type mechanism. Clearly, the contribution of the noble metal type mechanism to the DRM activity on the alpha-phase was more than that on the beta-phase, which was proposed to account for the better stability of the former than the latter. It was therefore suggested that the noble metal type mechanism should be preferable for DRM over carbide catalysts.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据