CERAMICS INTERNATIONAL
卷 43, 期 14, 页码 11218-11224出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2017.05.171
关键词
SiBNC fibres; Electron beam irradiation; Curing; Free radicals; Thermal stability
Curing green fibres infusible is an essential procedure for the preparation of SiBNC ceramic fibres. Previously, green fibres had been fabricated by one-pot synthesis of polyborosilazane (PBSZ) and melt-spinning. In this paper, we attempted to use the method of electron beam irradiation to crosslink green fibres. The variation of molecular structures from green fibres to cured fibres and the properties of sintered SiBNC fibres were investigated. Via electron beam irradiation, the free radicals are formed at the C atoms and Si atoms on the -N-SiH(CH3)- main chain units and terminal -Si(CH3)(3) groups. The radicals react with each other to produce cross linking, coupling and grafting among PBSZ chains, which all contribute to improvement of the cross-linking density of green fibres. The cured fibres performed a high ceramic yield of 80.4 wt%. After pyrolysis at 1500 degrees C, SiBNC ceramic fibres were acquired, which exhibited a good flexibility with 12 mu m in diameter and 1.22 GPa in tensile strength. The obtained fibres could remain amorphous up to 1700 degrees C and showed no mass loss at this temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据