This study investigates the combustion synthesis of AlN fibers using an NH4Cl additive and reports the effects of Al particle size (3, 30, and 180 mu m) and N-2 pressure (0.10, 0.25, and 0.50 MPa) on the purity and morphology of AlN fibers. The combustion temperature was directly measured during the synthesis to elucidate the formation mechanism of the AlN fibers. The phase purity and morphology of the products were studied using X-ray diffraction and scanning electron microscopy, respectively. When the particle size of Al was reduced from 180 to 3 mu m, the purity of the AlN product increased significantly owing to the large reaction area, which increased the combustion temperature. Furthermore, lower N-2 pressures enhanced the formation of AlN nanofibers due to the accelerated gasification of Al. The optimum values of the particle size of Al and the N-2 pressure for the formation of high-purity MN nanofibers were found to be 3 mu m and 0.10 MPa, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据