CONSTRUCTION AND BUILDING MATERIALS
卷 147, 期 -, 页码 815-826出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2017.04.186
关键词
Concrete; Corrosion; Steel reinforcements bars; Surface finish; Galvanized steel; Chlorides
资金
- PROVERICYT [IT573-10]
- PAICYT [IT720-11]
- SEP-CONACYT [CB-2012-01/177839]
- CONACYT [391931/256384]
The corrosion behavior of steel bars with different surface finish (ordinary (CS), dual phase (TTS) and galvanized (GS)) was studied in the laboratory using prismatic concrete specimens with two water/cement (w/c) ratios: 0.45 and 0.65. The specimens were exposed to penetration of chlorides using wetting and drying cycles for 2.6 years. The evolution with time of corrosion potential (E-corr) and polarization resistance (Rp) was studied. Microhardness, microstructural, chloride content and visual inspections of steel bars were also assessed. It was found that the different steels bars exposed followed a same sequence in depassivation for both w/c ratios; i.e. in this order: CS, TTS and GS. During initiation stage, the corrosion current density for TTS was lower than CS, similar behavior was observed in propagation stage for steel bars in specimens with w/c ratio of 0.45. The zinc-based coating obtained by hot-dip galvanization increases the time to corrosion initiation for CS bar and the amount of chlorides needed for this to occur. For GS and TTS bars, localized damage was observed, which was more severe for the GS bar. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据