期刊
APPLIED THERMAL ENGINEERING
卷 124, 期 -, 页码 454-465出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.applthermaleng.2017.06.003
关键词
Sorption enhanced chemical looping steam reforming (SE-CLSR); Ni-based oxygen transfer materials; Potassium promoted lithium zirconate; In-situ CO2 removal
资金
- Natural Science Foundation of China [51606046]
- International Science & Technology Cooperation Program of Guangzhou, China [2016201604030063]
Ni based oxygen transfer materials (OTMs) and Li2ZrO3 based sorbent have been synthesized for their potential use in a sorption enhanced chemical looping steam reforming (SE-CLSR) process. Ni based OTMs were firstly tested under chemical looping steam reforming (CLSR) process and the gaseous products with temperature variety during this process were measured and analyzed. Experimental results indicated that both of the OTMs exhibited good activities and stability during multiple glycerol reduction-air oxidation cycles towards H-2 production. The desired maximum hydrogen selectivities of 87.9% and 84.7% were obtained for NiO/NiAl2O4 and NiO/ZrO2 for steam to carbon ratio of 3 at 550 degrees C. The fuel feed step of reduction process could be divided into two periods with the OTMs possessing a dual function of oxygen carrier and catalyst. The decrease of conversions and selectivity for both OTMs was mainly due to the coke deposition, which reduced the catalytic effect in the reforming reaction as well as the oxygen transfer effect in the reduction reaction. Sorption enhanced chemical looping steam reforming (SE-CLSR) process for H-2 production with in-situ CO2 removal was carried out with OTM/sorbent ratio of 1 and multi-cyclic reaction/regeneration processes under 550 degrees C/850 degrees C with a steam/carbon ratio of 3 was also achieved. H-2 purity were both enhanced by the two OTMs and sorbent in SE-CLSR Therefore, it is possible to utilize oxygen from NiO and steam to oxidize glycerol, while enhancing the water-gas-shift reaction by capturing CO2 at the same time. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据